Polymer Polyols >>
More Details
CHP-2150
Introduction
Polymer polyols CHP-2150 which are based on general polyether polyols are synthesized by free radical graft polymerization with initiator and monomers of styrene and acrylonitrile under specific temperature and nitrogen protection. They are characterized by BHT free,low monomer residues,low viscosity and high solid content at 48%~52%. They gives a good flowabitily when mixing with water. The foam made by the products has low density gradient and uniform and fine cell structure. The products are mainly used in the ultra–high hardness flexible slabstock foams and flame lamination foams.
Specifications
Apperance Milky white viscous liquid Visual
Hydroxyl Value(mgKOH/g) 24-28   GB/T 12008.3-2009
Water Content(%) ≤0.05 GB/T 22313-2008/
ISO 14897:2002
pH 6-9 GB/T 12008.2-2010
Viscosity mPa·s(25℃) 4000-5500   GB/T 12008.7-2010
Residue of AN(ppm) ≤2 GB/T 31062-2014
Residue of SM(ppm) ≤25 GB/T 31062-2014
Solid Content(%) 48-52   GB/T 31062-2014

 

More Details
CHP-2045
Introduction
Polymer polyols CHP-2045 which are based on general polyether polyols are synthesized by free radical graft polymerization with initiator and monomers of styrene and acrylonitrile under specific temperature and nitrogen protection. They are characterized by BHT free, low monomer residues, low viscosity and high solid content at 44.5%-48.5%, They gives a good flowabitily when mixing with water.The foam made by the products has low density gradient and uniform and fine cell structure. The products are mainly used in the high hardness flexible slabstock foams and flame lamination foams.
Specifications
Apperance Milky white viscous liquid Visual
Hydroxyl Value(mgKOH/g) 26-30   GB/T 12008.3-2009
Water Content(%) ≤0.05 GB/T 22313-2008/
ISO 14897:2002
pH 6-9 GB/T 12008.2-2010
Viscosity  mPa·s(25℃) 3500-5000   GB/T 12008.7-2010
Residue of AN(ppm) ≤2 GB/T 31062-2014
Residue of SM(ppm) ≤25 GB/T 31062-2014
Solid Content(%) 44.5-48.5   GB/T 31062-2014

 

More Details
CHP-H30
Introduction
Polymer polyols CHP-H30 which are based on high active flexible foam polyether polyols are synthesized by free radical graft polymerization with initiator and monomers of styrene and acrylonitrile under specific temperature and nitrogen protection. At present they are important species of polyols applied in molded, flexible slabstock and semi-rigid polyurethane foams. They are BHT-free and amine-free high reactivity polymer polyols with low monomer residues, which are used for the high resilience slabstock foams, molded resilience foams,integral skin foams and semi-rigid polyurethane foams, etc.
Specifications
Apperance Milky white viscous liquid Visual
Hydroxyl Value(mgKOH/g) 22-27 GB/T 12008.3-2009
Water Content(%) ≤0.05 GB/T 22313-2008/
ISO 14897:2002
pH 5-8 GB/T 12008.2-2010
Viscosity  mPa·s(25℃) ≤3000 GB/T 12008.7-2010
Residue of AN(ppm) ≤2 GB/T 31062-2014
Residue of SM(ppm) ≤10 GB/T 31062-2014
Solid Content(%) 26-30 GB/T 31062-2014

 

More Details
CHP-H45
Introduction
Polymer polyols CHP-H45 which are based on high active flexible foam polyether polyols are synthesized by free radical graft polymerization with initiator and monomers of styrene and acrylonitrile under specific temperature and nitrogen protection. Currently they represent one of the most important groups of polyols for molded, flexible slabstock and semi-rigid polyurethane foams. They are BHT-free and amines-free high reactivity polymer polyols characterized by low viscosity, low monomer residues and high solid content at 41%-45%. The products are used to manufacture flexible and semi-rigid polyurethane foams of high load or highmodulus.
Specifications
Apperance Milky white viscous liquid Visual
Hydroxyl Value(mgKOH/g) 19-23 GB/T 12008.3-2009
Water Content(%) ≤0.05 GB/T 22313-2008/
ISO 14897:2002
pH 6-9 GB/T 12008.2-2010
Viscosity  mPa·s(25℃) ≤6000 GB/T 12008.7-2010
Residue of AN(ppm) ≤2 GB/T 31062-2014
Residue of SM(ppm) ≤10 GB/T 31062-2014
Solid Content(%) 41-45   GB/T 31062-2014

 

More Details
CHP-H50
Introduction
Polymer polyols CHP-H50 which are based on high active flexible foam polyether polyols are synthesized by free radical graft polymerization with initiator and monomers of styrene and acrylonitrile under specific temperature and nitrogen protection. Currently they represent one of the most important groups of polyols for molded, flexible slabstock and semi-rigid polyurethane foams. They are BHT-free and amines-free high reactivity polymer polyols characterized by low viscosity, low monomer residues and high solid content at 43%-50%. The products are used to manufacture flexible and semi-rigid polyurethane foams of high load or highmodulus.
Specifications

 

Apperance Milky white viscous liquid Visual
Hydroxyl Value(mgKOH/g) 17-21 GB/T 12008.3-2009
Water Content(%) ≤0.05 GB/T 22313-2008/
ISO 14897:2002
pH 6-9 GB/T 12008.2-2010
Viscosity  mPa·s(25℃) ≤9000 GB/T 12008.7-2010
Residue of AN(ppm) ≤2 GB/T 31062-2014
Residue of SM(ppm) ≤15 GB/T 31062-2014
Solid Content(%) 43-50 GB/T 31062-2014

 

Follow Us
Link
NEWS & MEDIA

ChangHua Chemical Technology Co.,Ltd.

No.20 Beijing Road Yangtze River International

Chemacal Industry Park,Zhangjiagang,jiangsu

TEL:0512-35003561

FAX:0512-35003522

ChangHua Chemical Technology Co.,Ltd.

No.20 Beijing Road Yangtze River International

Chemacal Industry Park,Zhangjiagang,jiangsu

TEL:0512-35003561

FAX:0512-35003522

Share
Terms of Use Contact Us Site Map
 Copyright©2017 ChangHua Chemical Technology Co.,Ltd. All rights reserved